WTR/APAO 复合改性沥青混合料性能研究

doi:10.19951/j.cnki.1672-9331.2022.01.004

长沙理工大学学报（自然科学版）

首页 > 过刊浏览>2022年第19卷第1期 >27-33. DOI:10.19951/j.cnki.1672-9331.2022.01.004

WTR/APAO 复合改性沥青混合料性能研究
DOI:
                        10.19951/j.cnki.1672-9331.2022.01.004
                    
CSTR:
                        [cstr]
                    
作者:
                        
                        
                    
作者单位:(1.郑州市公路工程公司,河南 郑州 450001;2.河南交院工程技术集团有限公司,河南 郑州 450061)
作者简介:尹建伟(1980-),男,高级工程师,主要从事公路与桥梁施工方面的研究。
通讯作者:尹建伟(1980-),男,高级工程师,主要从事公路与桥梁施工方面的研究。
中图分类号:U416.217
基金项目:国家自然科学基金资助项目(51408553)；河南省重点科技攻关计划项目 (152102210033)

Study on performance of WTR/APAO composite modified asphalt mixture

Author:

Affiliation:

(1.Zhengzhou City Highway Engineering Company,Zhengzhou 450001,China; 2.Henan Jiaoyuan Engineering Technology Group Co.,Ltd.,Zhengzhou 450061,China)

Fund Project:

摘要

图/表

访问统计

参考文献

相似文献

引证文献

资源附件

文章评论

摘要:

【目的】将复合改性沥青应用到沥青混合料当中,改善沥青路面的路用性能,延长其使用年限,提高服务水平。【方法】对70^{#^{沥青、SBS改性沥青、15% WTR 沥青、12% WTR+4%APAO 沥青及 15% WTR+ 4%APAO 沥青的 AC-13C 沥青混合料进行配合比设计；对上述5种不同沥青的 AC-13C 沥青混合料分别进行高温抗车辙、低温抗裂性、抗水损害、常温回弹模量及抗疲劳性能试验。【结果】上述5种沥青混合料的最佳油石比分别为4.6%、5.0%、5.1%、5.1%和5.3%;15% WTR+4%APAO 复合改性沥青混合料的高温、水稳定及抗疲劳性能最优,12%WTR+4%APAO 复合改性沥青混合料的25℃抗变形能力最优，SBS 改性沥青混合料的低温抗开裂性能最优。【结论】WTR/APAO 复合改性沥青混合料具有良好的路用性能，适合高等级沥青路面的铺设。}}

Abstract:

[Purposes]The composite modified asphalt was applied to asphalt mixture to im prove the road performance of asphalt pavement, prolong its service life and enhance its servicelevel. [Methods]The mix proportion of AC-13C asphalt mixture of 70^# asphalt, SBS modified asphalt, 15% WTR asphalt, 12% WTR+4% APAO asphalt and 15% WTR+4% APAO asphalt was designed. AC-13C asphalt mixtures of above five different asphalts were tested for high-temperature rutting resistance, low-temperature crack resistance, water damage resistance,normal-temperature resilience modulus and fatigue resistance. [Findings]The best oil-stone ratios of the five asphalt mixtures are 4.6%, 5.0%, 5.1%, 5.1% and 5.3%, respectively. 15% WTR+4% APAO composite modified asphalt mixture has the best performance of high-temperature,water stability and fatigue resistance, 12% WTR+4% APAO composite modified asphalt mixture has the best25 ℃ deformation resistance, and SBS modified asphalt mixture has the best low-temperature cracking resistance. [Conclusions]WTR/APAO composite modified asphalt mixture has good road performance and is suitable for high-grade asphalt pavement.

参考文献

相似文献

引证文献

引用本文

尹建伟,薛冰. WTR/APAO 复合改性沥青混合料性能研究[J].长沙理工大学学报（自然科学版）,2022,19(1):27-33.
YINJian-wei, XUEBing. Study on performance of WTR/APAO composite modified asphalt mixture[J]. Journal of Changsha University of Science & Technology (Natural Science),2022,19(1):27-33.

复制

文章指标

点击次数:
下载次数:
HTML阅读次数:
引用次数:

历史

收稿日期:
最后修改日期:
录用日期:
在线发布日期: 2022-04-10
出版日期:

引用本文

分享

文章指标

历史

文章二维码